Nylon 66 (dry as molded)
Nylon 66 polyamides are characterized by high strength, toughness, and resistance to abrasion, most chemicals, and repeated impact. Nylon 66 is a widely used polymer in many industries such as Automotive, Appliance, and Electrical/electronic.
Nylon 66 Specifications
|
Oxnilon 66-INJ |
Oxnilon 66-4IMP |
Oxnilon 66-15IMP |
Oxnilon 66 13GF |
Oxnilon 66 30GF |
Oxnilon 66 45GF |
| |
Description |
ASTM Test Method |
General Purpose, UL |
Medium Impact modified |
Superior Impact Modified, UL |
13% Glass Filled |
30% Glass Filled |
45% Glass Filled |
| Physical |
Melt Flow rate, g-10min |
D1238 |
|
|
|
|
|
|
|
Specific gravity |
D792 |
1.14 |
1.09 |
1.07 |
1.22 |
1.32 |
1.50 |
| |
Mold Shrinkage E-3 in/in |
D955 |
12-18 in/in |
14-20 in/in |
17-20 in/in |
4-6 in/in |
2-4 in/in |
2-4 in/in |
|
Tensile Strength Break, PSI |
D638 |
12,000 |
9,000 |
7,500 |
16,000 |
22,500 |
25,000 |
|
Tensile Strength Yield, PSI |
D638 |
12,000 |
8,700 |
7,300 |
16,000 |
22,500 |
25,000 |
| Mechanical |
Flexural Strength, PSI |
D790 |
16,500 |
12,000 |
9,000 |
23,000 |
30,000 |
34,000 |
|
Flexural Modulus, PSI x 1000 |
D790 |
410 |
280 |
245 |
685 |
1,100 |
1,600 |
|
Notched Izod Impact strength ft-lb/in |
D256 |
1.0 |
3.0 |
15.0 |
1.2 |
1.6 |
2.5 |
| |
Gardner Falling Dart Impact in-lbs |
D3029 |
|
|
|
|
|
|
| Thermal* |
HDT @66 PSI F |
D648 |
445 |
440 |
415 |
465 |
485 |
490 |
| |
HDT @264 PSI F |
D648 |
190 |
165 |
155 |
450 |
460 |
465 |
| Flammability |
UL 94 @1/16" |
UL94 |
V-2 |
HB |
HB |
HB |
HB |
HB |
| |
UL 94 @1/8" |
UL94 |
|
|
|
|
|
|
|
Processing method***** |
|
IM |
IM |
IM |
IM |
IM |
IM |
|
Drying Temp F |
|
165-185 |
165-185 |
165-185 |
165-185 |
165-185 |
165-185 |
| Typical Processing Conditions Units |
drying Time(hours) |
|
3-4** |
3-4** |
3-4** |
3-4** |
3-4** |
3-4** |
|
Melt Temp (F) |
|
530-560 |
530-560 |
530-560 |
550-570 |
550-570 |
550-570 |
|
Mold temp(F) |
|
150-200 |
150-200 |
150-200 |
150-220 |
150-220 |
150-220 |
|
Front Zone(F) |
|
530-550 |
530-550 |
530-550 |
560-580 |
560-580 |
560-580 |
|
Middle Zone(F) |
|
520-540 |
520-540 |
520-540 |
530-550 |
530-550 |
530-550 |
| |
Rear Zone(F) |
|
510-530 |
510-530 |
510-530 |
520-540 |
520-540 |
520-540 |
|
* All mechanical and thermal testing conducted on
1/8 thick unpigmeneted test samples
|
|
(Structural foam grades tested with foamed parts,
with a 10-20% weight reduction.) |
|
** Do not exceed 8 hours |
|
*** Do not exceed 24 hours |
|
****Processing Methods: Injection molding (IM), Structural Foam (SF), Extrusion (E) |
|
Notched Izod @ 40F, ft-lb/in. ASTM D256 |
|
|